Abstract

In this study, in the four colors of red polyester fabric, blue polyester fabric, green polyester fabric, and yellow polyester fabric, the L value will decrease as the concentration increases, and the LUX value will also decrease. It can be known that the L value of the red polyester cloth and the red polyester cloth plus the luminescent film are analyzed at different concentrations. When the concentration of the red polyester cloth is 0.1%, the L value is 51.43, and the red polyester cloth concentration is 2%. The L value was 44.6, the L value was 52.25 when the red polyester cloth plus luminescent sheet concentration was 0.1%, and the L value was 45.77 when the red polyester cloth plus luminescent sheet concentration was 2%. The L value of different concentrations of the yellow polyester cloth and the fluorescent yellow and the luminescent film were measured. The L value decreased with the increase in the concentration of the yellow polyester cloth from 0.1% to 2%. When the minimum concentration of the yellow polyester cloth is below 0.1% to 2%, the L value will decrease as the concentration increases, and the minimum concentration after the yellow polyester cloth and the fluorescent yellow and the cold light sheet are affixed is 0.1. From 2% to 2%, the L value decreases as the concentration increases.

• Electroluminescence
• Lab value
• brightness

摘要

本研究是以在紅色聚酯布、藍色聚酯布、綠色聚酯布、黃色聚酯布等四種顏色會隨著濃度上升，L值會隨之下降，LUX值也會隨之下降。可得知紅色聚酯布與紅色聚酯布加冷光片之不同濃度進行的L值分析，實驗得知紅色聚酯布濃度為0.1%時，L值為51.43，紅色聚酯布濃度為2%時，L值為44.6，紅色聚酯布加冷光片濃度為0.1%時，L值為52.25，紅色聚酯布加冷光片濃度為2%時，L值為45.77。並佐證黃色聚酯布和螢光黃與冷光片貼合後之不同濃度進行的L值分析，黃色聚酯布從濃度為0.1%至2%時，隨著濃度增加，L值會隨之下降，黃色聚酯布貼合冷光片後最低濃度為0.1%至2%時，隨著濃度增加，L值會隨之下降，黃色聚酯布與螢光黃與冷光片貼合後最低濃度為0.1%至2%時，隨著濃度增加，L值會隨之下降。

• 冷光片
• Lab值
• 亮度

• Study of Blended TPU/ PA 6 Composite Electrospinning Nonwoven for Blocking Aerosol Particles
  I-Chen Yang, Ya-Xuan Chiu, Shuo-Qi Zeng, Yi-Jun Pan
• Celebration & Dress
  Pi Jing Ferng, Wen Kuei Lai
• Evaluation and Test of Sulfonation Upgrading Performance of PVA Proton Exchange Membrane
  Wan-Ling Liao, Chih-Hung He, Mei-Feng Lai, Ching-Wen Lou, Jia-Horng Lin
• Flame Retardancy and Properties Evaluation of Polyurethane Foam by Adding AlginatePolyurethane Foam by Adding Alginate
  Kai-Xiang Jiang, Ruei-Ren Ou, Chen-Hung Huang, Ching-Wen Lou, Jia-Horng Lin
• Study about the Absorbing Moisture Evaluation of the Inner Layer in Sweat pants
  C. H. Chan, W. H. Hsing