第 21 卷第 2 期（2014）

人的腳部會因為長時間在戶外走動，經過風吹、日曬、雨淋後造成腳部悶熱、不適，進而導致腳部受到細菌感染，產生香港腳等腳部疾病。若鞋內織物具有良好的抑菌效果，可使鞋內的細菌不再繼續滋生，達到腳部健康衛生的效果。本實驗以聚酯針軋不織布為基材，採用奈米銀抑菌劑，目的是為了尋找合適的加工條件，使不織布具有良好的抑菌效果亦節省成本，以提供業界作為製造參考依據。經由實驗觀察，未添加壓克力樹脂之抑菌劑在室溫下會產生褐色斑，有變色現象。本研究以金黃色葡萄球菌及肺炎桿菌測試其抑菌效果得到，60、90、120ppm之奈米銀抑菌劑添加及未添加壓克力樹脂之布樣上菌無大量孳生，皆有抑菌效果，但效果不明顯。

People used to have a long walk outdoors, after wind, sun, rain causing foot muggy and discomfort. Bacterial infection leading to leg. Influence by athlete's foot or another foot`s disease. If shoes would have great antibacterial effects, can make bacterial never ever breeding in the shoes. Measure up the effect of health and hygiene of foots. The experiment use the Rolling Pin Non-Woven and Nano-Antibacterial Agent to find out the best processing conditions, can make the Rolling Pin Non-Woven have great antibacterial effects also can province money. Provide a reference for manufacturing indu…

本實驗的目的在於探討玻璃纖維基布經由水性PU多層塗布，並且在各樹脂層上噴印部分圖案時，改變塗布刀狹縫高度，使其達到多層次效果。由實驗結果得知第一層至第四層塗布刀狹縫高度分別設定為100μm、150μm、150μm、150μm有最好的表面形態與厚度；透光度的分析可得知，隨著樹脂層的增加其透光率逐漸從22%降到18.63%；立體度的分析可得知，隨著樹脂層的增加背景色逐漸模糊，而花朵的邊緣則逐漸銳利，確立本實驗確實有達到立體之效果。

The research is glass fabric multilayer coating by Waterborne Polyurethane, and on each resin phase print part graphics, change the height of the coated knife slit to achieve multi- level effect. Base on the experimental results the height of the coated knife slit from one sets respect 100?m, 150?m, 150?m, 150?m, which can get the best coating effect; by analysis of the transmittance knowable, along with increment of the resin layer transmittance are down from 22% to 18.63%; by analysis of the stereo degree knowable, along with increment background of the resin layer the color is gradual blur…

時尚產品並非適合網路行銷的標準品，目標顧客是網路購物金額較少的年輕女性，但仍有不少成功的網路平價時尚品牌公司，因此這些消費者特性如理解層級、價格敏感度及時尚喜好度等就值得深入討論，本研究先收集消費者理解層級內容，依此設計問卷，再利用網路問卷進行量化資料收集，分析年輕女性理解層級、時尚喜愛程度及價格敏感度對網路時尚品牌評價的影響。 網路購買平價時尚品牌消費者（1008個受訪者）以18-26歲、專科/大學、每月平均上網瀏覽次數多在4次以上，每月平均服飾花費以1,001-3,000元，花費在特定袋包上有201-500元最多。本研究透過方法目的鏈去了解購買網路時尚品牌包包消費者最大價值為心靈滿足，平價是購買動機，包包流行時尚的整體造型及良好的物品收納功能是利益。消費者對品牌理解程度愈高，品牌評價就愈高，價格敏感度（負相關）及時尚喜好度（正相關）均對理解層級具有調節效果。

Fashion products which are not standardized products are not suitable to be sold through internet. The purchasing expenses of young ladies who are the main consumers for internet fashion products are lower than others. However, there are still many successful internet brands of cheap and fashion. Therefore, consumers’ traits such as price sensitivity, preference of liking and understanding chains are worth discussing. We collected the contexts of consumers’ understanding chains to design questionnaires. The internet questionnaires were used to collect quantitative data to analyze factors …

安全防護衣物的需求量遽增且要求規範也愈嚴格，而防彈防護衣物的關鍵原料在於高強力纖維，且在新的規範中亦需提高防穿刺能力，故本實驗使用超高分子量聚乙烯纖維做為基布，以電漿處理表面產生官能基，以及使用不同貼合膠黏附後，探討不同PU複合材的強力以及其衝擊強度、與防穿刺強度之差別，及添加複合材重量前後變化所造成之影響。

Demand for safety protective clothing addition and strict regulated, the key raw material for bullet-proof protective clothing is a high-strength fibers, also need the ability to raise anti-puncture and the new specification, the experimental use of ultra-high molecular weight polyethylene fiber as the base fabric, functional groups to the surface of the plasma treatment, Peel strength as well as the use of different bonding glue adhesion of the PU bonding glue and the impact strength, and anti-puncture strength of the difference, and adding the impact caused by changes in the weight of the g…

本實驗使用聚丙烯纖維、椰子纖維，不同纖維用量製作板材厚度，改變纖維之用量，加入發泡劑後，混和製成複合吸音用板材。相較於市面上的板材，吸收水分導致損耗，藉由我們吸水率、含水率、衝擊力、吸音性測試後，希望板材能得到吸水率降低及衝擊力提升及吸音性效果。

The experimental use of polypropylene fiber, coconut fiber, The amount of production of different fiber sheet thickness, changes in fiber consumption, adding foaming agent, mixed with sound-absorbing panels made of composite, compared to the market of the plate, loss due to moisture absorption, with our relevant tests, Hoping to get lower and impact absorption enhancing effect.

本研究以纏繞成型法製作玄武岩纖維複合材料預浸材，再以手排疊法將纖維以平行的方式進行疊層，並熱壓成型，製作玄武岩纖維/酚醛樹脂複合板材，主要探討纖維含有率對複合材料拉伸強力、限氧指數(LOI值)、碳化層面積、背面溫度的影響。結果發現，當玄武岩纖維含有率上升時，其拉伸力學性質愈佳，防火性能卻下降。

In this study, filament-wound basalt fiber reinforced phenolic resin composites prepreg were made, and then, manual fibers were stacked and laminated in parallel, and thermoforming, production of basalt fiber reinforced phenolic resin composite . Focuses on fiber content of the composite tensile strength, limiting oxygen index, carbide layer area, the impact on the back of temperature. It was found that when the basalt fiber content rises, the better tensile mechanical properties, fire performance has declined.

本研究是利用液中硬化法透過自組裝設備製備出單核型海藻酸鈉微膠囊，以海藻酸鈉為殼材，樟腦油為芯材，藉由改變殼材濃度及交聯劑濃度探討其釋放性差異並計算包覆率，觀察成形性及其粒徑。由實驗結果顯示，殼材濃度較低之海藻酸鈉微膠囊釋放時間較長釋放量較高，因殼材濃度較高時其分子結構較緊密較不易穿透而造成釋放效果較差，同時在不同殼材濃度與不同交聯劑下所製備出之單核海藻酸鈉微膠囊其包覆率皆在95%以上，當殼材海藻酸鈉濃度由0.75~1.75wt%逐漸增加時，其粒徑亦隨之增大。

This study was conducted using through home-made equipment by an orifice method to make the single core alginate microcapsule. The sodium alginate was used as wall material and the core material is camphor oil. In order to measure the different degree of release, calculating encapsulated ratio and the average size of the microcapsule, a variety of concentrations of shell material and cross-linking agent were used. The result indicated that the longer release amount of releasing time is relatively high when the concentrations of shell material lower. The result-ing effect is a result of poor r…

本研究係以芭蕉纖維作為無土栽培介質，利用芭蕉纖維與溴化十六烷基三甲銨(CTAB)水溶液(0.5wt%、1.0wt%、1.5wt%、2.0wt%、2.5wt%)和海藻酸鈉水溶液(3.0wt%)，均勻混合後，製作無土栽培之樣本。文中探討添加不同濃度溴化十六烷基三甲銨(CTAB)水溶液 (0.5wt%、1.0wt%、1.5wt%、2.0wt%、2.5wt%)與芭蕉纖維混合後對其成型性、含水率、保水率、pH值和EC值之影響。由實驗結果顯示，以添加CTAB 2.5wt%樣本之成型性最佳，含水率以添加CTAB0.5wt%之最佳，未添加海藻酸鈉樣本之保水時間皆達66小時；添加海藻酸鈉樣本之保水時間皆達95個小時，pH值約在4.5~5之間，EC值以添加CTAB0.5wt%樣本為最佳，其EC值為0.71mS/cm，符合在植物栽培環境。

The soilless culture medium were prepared by microwave foaming method with banana fiber with different concentration hexadecyl trimethyl ammonium bromide (CTAB) 0.5wt%、1.0wt%、1.5wt%、2.0wt%、2.5wt%, respectively and sodium alginate 3.0wt%. The samples were used 3.0wt% Calcium Chloride (CaCl2) for crosslink reaction. Here, we analyses formability, moisture content, water retention, and value of pH and EC of microwave foaming method with banana fiber, and the effect of different concentration hexadecyl trimethyl ammonium bromide (CTAB) addition and sodium alginate 3.0%. The experimental result in…